Metal-Free Lewis Pair Catalysts for a One-Pot Terpolymerization of Propylene Oxide, ʟ-Lactide and CO2

Sustainable Polymer & Energy. 2023, 1(1), 10002; https://doi.org/10.35534/spe.2023.10002
Shuxian Ye 1    Jiaxin Liang 1    Yansong Ren 1    Shuanjin Wang 1    Dongmei Han 4    Sheng Huang 1    Zhiheng Huang 1    Min Xiao 1 *    Yuezhong Meng 1,2,3,4 *   
1
The Key Laboratory of Low-carbon Chemistry & Energy Conservation of Guangdong Province/State Key Laboratory of Optoelectronic Materials and Technologies, School of Materials Science and Engineering, Sun Yat-sen University, Guangzhou 510275, China
2
Institute of Chemistry, Henan Academy of Sciences, Zhengzhou 450000, China
3
Research Center of Green Catalysts, College of Chemistry, Zhengzhou University, Zhengzhou 450001, China
4
School of Chemical Engineering and Technology, Sun Yat-sen University, Guangzhou 510275, China
*
Authors to whom correspondence should be addressed.

Received: 27 Nov 2022    Accepted: 11 Jan 2023    Published: 30 Jan 2023   

Abstract

Multiblock and di-/tri-block copolymers are successfully synthesized for the first time via the metal-free terpolymerization of propylene oxide (PO), ʟ-lactide (LA) and CO2 in one-pot/one-step and one-pot/two-step protocols respectively. Firstly, triethyl borane (TEB) and bis(triphenylphosphine)iminium chloride (PPNCl) Lewis pair is employed in the ring-opening polymerization of LA, wherein the catalytic efficiency is significantly correlated to the TEB/PPNCl feed ratio. Next, a series of TEB/base pairs are selected to synthesize the PO/LA/CO2 terpolymer (PPCLA) in one-pot/one-step strategy. In PPCLA synthesis, LA exhibits the fastest reaction rate but the severe transesterification is almost unavoidable, resulting in low molecular weight products. In order to prepare high-molecular-weight terpolymers, a one-pot/two-step methodology has to be applied. By this method, the copolymerization of PO/CO2 proceeds first to form poly(propylene carbonate) (PPC) macroinitiators, which triggers the polymerization of LA to polylactide (PLA), leading to PLA-PPC or PLA-PPC-PLA block copolymers. The synthesized PLA-PPC-PLA block copolymers display an improved thermal stability compared with PPC.

References

1.
Zhang X, Fevre M, Jones GO, Waymouth RM. Catalysis as an enabling science for sustainable polymers. Chem. Rev. 2018, 118, 839–885. [Google Scholar]
2.
Tang S, Nozaki K. Advances in the synthesis of copolymers from carbon dioxide, dienes, and olefins. Acc. Chem. Res. 2022, 55, 1524–1532. [Google Scholar]
3.
Bhat GA, Darensbourg DJ. Progress in the catalytic reactions of CO2 and epoxides to selectively provide cyclic or polymeric carbonates. Green Chem. 2022, 24, 5007–5034. [Google Scholar]
4.
Wu J, Yu TL, Chen CT, Lin CC. Recent developments in main group metal complexes catalyzed/initiated polymerization of lactides and related cyclic esters. Coord. Chem. Rev. 2006, 250, 602–626. [Google Scholar]
5.
Xu Y, Lin L, Xiao M, Wang S, Smith AT, Sun L, et al. Synthesis and properties of CO2-based plastics: Environmentally-friendly, energy-saving and biomedical polymeric materials. Prog. Polym. Sci. 2018, 80, 163–182. [Google Scholar]
6.
Nampoothiri KM, Nair NR, John RP. An overview of the recent developments in polylactide (PLA) research. Bioresour. Technol. 2010, 101, 8493–8501. [Google Scholar]
7.
Rasal RM, Janorkar AV, Hirt DE. Poly(lactic acid) modifications. Prog. Polym. Sci. 2010, 35, 338–356. [Google Scholar]
8.
Hamad K, Kaseem M, Ayyoob M, Joo J, Deri F. Polylactic acid blends: The future of green, light and tough. Prog. Polym. Sci. 2018, 85, 83–127. [Google Scholar]
9.
Bednarek M. Branched aliphatic polyesters by ring-opening (co)polymerization. Prog. Polym. Sci. 2016, 58, 27–58. [Google Scholar]
10.
Luinstra G. Poly(propylene carbonate), old copolymers of propylene oxide and carbon dioxide with new interests: Catalysis and material properties. Polym. Rev. 2008, 48, 192–219. [Google Scholar]
11.
Liu SQ, Wang JL, Huang KL, Liu YF, Wu WK. Synthesis of poly(propylene-co-lactide carbonate) and hydrolysis of the terpolymer. Polym. Bull. 2011, 66, 327–340. [Google Scholar]
12.
Tang L, Luo W, Xiao M, Wang S, Meng Y. One-pot synthesis of terpolymers with long ʟ-lactide rich sequence derived from propylene oxide, CO2, and ʟ-lactide catalyzed by zinc adipate. J. Polym. Sci. A Polym. Chem. 2015, 53, 1734–1741. [Google Scholar]
13.
Song P, Xu H, Mao X, Liu X, Wang L. A one-step strategy for aliphatic poly(carbonate-ester)s with high performance derived from CO2, propylene oxide and ʟ-lactide. Polym. Adv. Technol. 2017, 28, 736–741. [Google Scholar]
14.
Xie D, Yang Z, Wu L, Zhang C, Chisholm MH. One-pot regioselective and stereoselective terpolymerization of rac-lactide, CO2 and rac-propylene oxide with TPPMCl (M = Cr, Co, Al)/PPNCl binary catalyst. Polym. Int. 2018, 67, 883–893. [Google Scholar]
15.
Li X, Hu C, Pang X, Duan R, Chen X. One-pot copolymerization of epoxides/carbon dioxide and lactide using a ternary catalyst system. Catal. Sci. Technol. 2018, 8, 6452–6457. [Google Scholar]
16.
Duan R, Hu C, Sun Z, Zhang H, Pang X, Chen X. Conjugated tri-nuclear salen-Co complexes for the copolymerization of epoxides/CO2: Cocatalyst-free catalysis. Green Chem. 2019, 21, 4723–4731. [Google Scholar]
17.
Wu GP, Darensbourg DJ, Lu XB. Tandem metal-coordination copolymerization and organocatalytic ring-opening polymerization via water to synthesize diblock copolymers of styrene oxide/CO2 and lactide. J. Am. Chem. Soc. 2012, 134, 17739–17745. [Google Scholar]
18.
Lohmeijer BGG, Pratt RC, Leibfarth F, Logan JW, Hedrick JL. Guanidine and amidine organocatalysts for ring-opening polymerization of cyclic esters. Macromolecules 2006, 39, 8574–8583. [Google Scholar]
19.
Darensbourg DJ, Wu G. A one-pot synthesis of a triblock copolymer from propylene oxide/carbon dioxide and lactide: Intermediacy of polyol initiators. Angew. Chem. Int. Ed. 2013, 52, 10602–10606. [Google Scholar]
20.
Wu GP, Darensbourg DJ. Mechanistic insights into water-mediated tandem catalysis of metal-coordination CO2/epoxide copolymerization and organocatalytic ring-opening polymerization: One-pot, two steps, and three catalysis cycles for triblock copolymers synthesis. Macromolecules 2016, 49, 807–814. [Google Scholar]
21.
Hu C, Duan R, Yang S, Pang X, Chen X. CO2 controlled catalysis: Switchable homopolymerization and copolymerization. Macromolecules 2018, 51, 4699–4704. [Google Scholar]
22.
Zhang D, Boopathi SK, Hadjichristidis N, Gnanou Y, Feng X. Metal-free alternating copolymerization of CO2 with epoxides: Fulfilling “green” synthesis and activity. J. Am. Chem. Soc. 2016, 138, 11117–111120. [Google Scholar]
23.
Wang Y, Zhang JY, Yang JL, Zhang HK, Kiriratnikom J, Zhang CJ, et al. Highly selective and productive synthesis of a carbon dioxide-based copolymer upon zwitterionic growth. Macromolecules 2021, 54, 2178–2186. [Google Scholar]
24.
Chen Z, Yang JL, Lu XY, Hu LF, Cao XH, Wu GP, et al. Triethyl borane-regulated selective production of polycarbonates and cyclic carbonates for the coupling reaction of CO2 with epoxides. Polym. Chem. 2019, 10, 3621–3628. [Google Scholar]
25.
Patil NG, Boopathi SK, Alagi P, Hadjichristidis N, Gnanou Y, Feng X. Carboxylate salts as ideal initiators for the metal-free copolymerization of CO2 with epoxides: Synthesis of well-defined polycarbonates diols and polyols. Macromolecules 2019, 52, 2431–2438. [Google Scholar]
26.
Papagiannopoulos A, Zhao J, Zhang G, Pispas S, Jafta CJ. Viscosity transitions driven by thermoresponsive self-assembly in PHOS-g-P(PO-r-EO) brush copolymer. Macromolecules 2018, 51, 1644–1653. [Google Scholar]
27.
Chen Y, Shen J, Liu S, Zhao J, Wang Y, Zhang G. High efficiency organic Lewis pair catalyst for ring-opening polymerization of epoxides with chemoselectivity. Macromolecules 2018, 51, 8286–8297. [Google Scholar]
28.
Zhang C, Duan H, Hu L, Zhang C, Zhang X. Metal-free route to precise synthesis of poly(propylene oxide) and its blocks with high activity. ChemSusChem 2018, 11, 4209–4213. [Google Scholar]
29.
Boopathi SK, Hadjichristidis N, Gnanou Y, Feng X. Direct access to poly(glycidyl azide) and its copolymers through anionic (co-)polymerization of glycidyl azide. Nat. Commun. 2019, 10, 293. [Google Scholar]
30.
Hu L, Zhang C, Wu H, Yang J, Liu B, Duan H, et al. Highly active organic Lewis pairs for the copolymerization of epoxides with cyclic anhydrides: Metal-free access to well-defined aliphatic polyesters. Macromolecules 2018, 51, 3126–3134. [Google Scholar]
31.
Zhu S, Wang Y, Ding W, Zhou X, Liao Y, Xie X. Lewis pair catalyzed highly selective polymerization for the one-step synthesis of AzCy(AB)xCyAz pentablock terpolymers. Polym. Chem. 2020, 11, 1691–1695. [Google Scholar]
32.
Kummari A, Pappuru S, Chakraborty D. Fully alternating and regioselective ring-opening copolymerization of phthalic anhydride with epoxides using highly active metal-free Lewis pairs as a catalyst. Polym. Chem. 2018, 9, 4052–4062. [Google Scholar]
33.
Zhang B, Li H, Luo H, Zhao J. Ring-opening alternating copolymerization of epichlorohydrin and cyclic anhydrides using single- and two-component metal-free catalysts. Eur. Polym. J. 2020, 134, 109820. [Google Scholar]
34.
Ji HY, Chen XL, Wang B, Pan L, Li YS. Metal-free, regioselective and stereoregular alternating copolymerization of monosubstituted epoxides and tricyclic anhydrides. Green Chem. 2018, 20, 3963–3973. [Google Scholar]
35.
Li H, He G, Chen Y, Zhao J, Zhang G. One-step approach to polyester–polyether block copolymers using highly tunable bicomponent catalyst. ACS Macro Lett. 2019, 8, 973–978. [Google Scholar]
36.
Ji HY, Song DP, Wang B, Pan L, Li YS. Organic Lewis pairs for selective copolymerization of epoxides with anhydrides to access sequence-controlled block copolymers. Green Chem. 2019, 21, 6123–6132. [Google Scholar]
37.
Liu S, Bai T, Ni K, Chen Y, Zhao J, Ling J, et al. Biased Lewis pair: A general catalytic approach to ether-ester block copolymers with unlimited sequences. Angew. Chem. Int. Ed. 2019, 58, 15478–15487. [Google Scholar]
38.
Varghese JK, Hadjichristidis N, Gnanou Y, Feng X. Degradable poly(ethylene oxide) through metal-free copolymerization of ethylene oxide with ʟ-lactide. Polym. Chem. 2019, 10, 3764–3771. [Google Scholar]
39.
Chidara VK, Boopathi SK, Hadjichristidis N, Gnanou Y, Feng X. Triethylborane-assisted synthesis of random and block poly(ester-carbonate)s through one-pot terpolymerization of epoxides, CO2, and cyclic anhydrides. Macromolecules 2021, 54, 2711–2719. [Google Scholar]
40.
Liang J, Ye S, Wang W, Fan C, Wang S, Han D, et al. Performance tailorable terpolymers synthesized from carbon dioxide, phthalic anhydride and propylene oxide using Lewis acid-base dual catalysts. J. CO2 Util. 2021, 49, 101558. [Google Scholar]
41.
Ye S, Wang W, Liang J, Wang S, Xiao M, Meng Y. Metal-free approach for a one-pot construction of biodegradable block copolymers from epoxides, phthalic anhydride, and CO2. ACS Sustain. Chem. Eng. 2020, 8, 17860–17867. [Google Scholar]
42.
Zhang J, Wang L, Liu S, Kang X, Li Z. A Lewis pair as organocatalyst for one-pot synthesis of block copolymers from a mixture of epoxide, anhydride, and CO2. Macromolecules 2021, 54, 763–772. [Google Scholar]
43.
Yang J, Wu H, Li Y, Zhang X, Darensbourg DJ. Perfectly alternating and regioselective copolymerization of carbonyl sulfide and epoxides by metal-free Lewis pairs. Angew. Chem. Int. Ed. 2017, 56, 5774–5779. [Google Scholar]
44.
Hošťálek Z, Trhlíková O, Walterová Z, Martinez T, Peruch F, Cramail H, et al. Alternating copolymerization of epoxides with anhydrides initiated by organic bases. Eur. Polym. J. 2017, 88, 433–447. [Google Scholar]
45.
Zhang D, Feng X, Gnanou Y, Huang K. Theoretical mechanistic investigation into metal-free alternating copolymerization of CO2 and epoxides: The key role of triethylborane. Macromolecules 2018, 51, 5600–5607. [Google Scholar]
Creative Commons

© 2024 by the authors; licensee SCIEPublish, SCISCAN co. Ltd. This article is an open access article distributed under the CC BY license (https://creativecommons.org/licenses/by/4.0/).